Zheflon® FL2608 Copolymer PVDF- Injection Grade
FL2608 PVDF copolymer is low viscosity grade, suitable for applications in the cable industry.
| Produktkatalog | PVDF |
|---|---|
| Marke | Zheflon PVDF & Flurine FKM Manufacturer |
| Modell | FL2608 |
| Features | Copolymer, Low viscosity |
| Uses | Wire, Cable |
| Forms | Translucent white particles |
| Processing technology | Suspension PVDF |
| Aktualisierungszeit | 2024/11/21 |
Detailed Info
Zheflon®FL2608 PVDF copolymer is low viscosity grade, especially suitable for applications in the cable industry. It gives the cable excellent mechanical properties, flexibility and electrical performance; high temperature corrosion resistance; low flammability, smoke emission. In addition, the zero-perfluorooctanoic acid and heavy metal content to comply with RoHS requirements.
General | ||
Features | Copolymer, Low viscosity | |
Uses | Wire, Cable | |
Forms | Translucent white particles | |
Items | Typical Value FL2608 | Test Method |
Physical Properties | ||
Density（g/cc） | 1.77~1.80 | ASTM D792 |
Melt Flow Rate（g/10min） | 15.0~25.0 | Load 5kg，230℃，ASTM D1238 |
Melt viscosity（Kps） | 6~9 | Shear Rate 100 1/s，ASTM D3835 |
Water Absorption（%）（Time 24 hr） | ≤0.040 | ISO 62 |
Linear Mold Shrinkage（cm/cm） | 0.0200~0.0300 | |
Molecular Properties | ||
Molecular weight（Da） | 250,000~280,000 | GPC,DMF,ISO 16014 |
Intrinsic viscosity（dl/g） | 0.85~1.00 | 30℃,DMAC |
Molecular weight distribution | 2.0-3.0 | GPC,DMF,ISO 16014 |
Mechanical Properties | ||
Tensile Modulus（Thickness2.00mm）（MPa） | 600~1000 | 1.0mm/min,ASTM D638 |
Flexural Modulus（Thickness2.00mm）（MPa） | 800~1000 | 2.0mm/min,ASTM D790 |
Yield Strength（Thickness2.00mm）（MPa） | 25.0~35.0 | 50mm/min,ASTM D638 |
Break Strength（Thickness2.00mm）（MPa） | 20.0~30.0 | 50mm/min,ASTM D638 |
Elongation at Yield（%） | 10.0~15.0 | 50mm/min,ASTM D638 |
Elongation at Break（%） | 200~600 | 50mm/min,ASTM D638 |
Hardness, Shore D（Thickness2.00mm） | 70~75 | ASTM D2240 |
Izod Impact, Notched（Thickness 4.00mm, 23℃）（J/m） | 100~150 | Notched V 10 mm ASTM D256 |
Thermal Properties | ||
Melting Point（℃） | 158~166 | ASTM D3418 |
Crystallization Temperature（DSC peak）（℃） | 115~130 | ASTM D3418 |
Glass Transition Temp, Tg（℃） | -32.0 | ASTM E1356 |
Decomposition Temperature（℃） | 330~350 | 1% wt. loss / in air |
Vicat Softening Point（℃） | 90~105 | ASTM D1525 |
Heat deflection temperature at 1.8 MPa（Thickness 4.00mm）（℃） | 50~60 | After annealing 150℃,16h ASTM D648 |
Electrical Properties | ||
Surface Resistance（ohm） | ≥1.00E+14 | Voltage<1V，After 2 min—500V ASTM D257 |
Electrical Resistivity（ohm·cm） | ≥1.00E+14 | Intensity=10mA，After 2 min@23℃ ASTM D257 |
Dielectric strength（Thickness 1.00mm,23℃）（KV/mm） | 20~25 | ASTM D149 |
Dielectric constant（1kHz,23℃） | 7.0~10.0 | ASTM D150 |
Burning Properties | ||
UL Flame retardant grade（0.100mm） | V-0 | UL94 |
Oxygen Index（3.00mm） | 44% | ASTM D2683 |
Kontaktieren Sie uns umgehend
Wir verfügen über ein engagiertes Team technischer Experten, das Sie bei Ihren anspruchsvollsten Projekten unterstützt. Entdecken Sie kostengünstige, maßgeschneiderte Lösungen für außergewöhnliche Leistung und Wert. Kontaktieren Sie uns noch heute – wir nehmen die Herausforderung gerne an!
- Name
- Telefon
- *Titel
- *Inhalt
Produkte
Lassen Sie uns gemeinsam innovativ sein
Wir verfügen über ein engagiertes Team technischer Experten, das Ihnen bei Ihren anspruchsvollsten Projekten hilft. Kontaktieren Sie uns noch heute – wir sind bereit für die Herausforderung!
Das 2007 gegründete Technologieunternehmen ist auf fluorbasierte Materialien spezialisiert. Wir treiben erneuerbare Energien und Nachhaltigkeit durch Innovation voran.